发表刊物：POLYMER CHEMISTRY

收录刊物：SCIE、EI

卷号：10

期号：24

页面范围：3371-3379

ISSN号：1759-9954

摘要：Nitrogen-rich microporous polymers that contain different contents of primary, secondary and tertiary amine groups in their networks are prepared via the amine-formamido condensation reaction utilizing formamide, formohydrazide, N-methylformamide and N,N-dimethylformamide as starting monomers to polymerize with melamine, respectively, via a facile one-step polymerization reaction in the absence of any catalyst. The resultant four polymers exhibit BET surface areas of 612-748 m(2) g(-1) and adjustable pores sizes in the range from 0.52 to 1.10 nm. The systematically changed types of amine groups and porosity parameters result in interesting variations of interfacial interactions between the porous surface and CO2 molecule, so as to significantly influence the adsorption behaviour of CO2 gas. The uptake of CO2 in polymers is up to 14.6 wt% (273 K/1.0 bar) with an outstandingly high CO2/N-2 adsorption selectivity of 151. Moreover, after adding a small amount of water vapour in the mixed CO2/N-2 gas, the adsorption selectivity CO2/N-2 further increases to 173. The adsorption of CO2 and its selectivity over N-2 in this series of microporous polymers under both dry and humid conditions are studied and discussed in terms of the type of the amine group on the polymer skeletons, the adsorption mechanism and the porosity parameters.