点击次数：

论文类型：期刊论文

发表时间：2013-02-21

发表刊物：POLYMER CHEMISTRY

收录刊物：SCIE、EI、Scopus

卷号：4

期号：4

页面范围：961-968

ISSN号：1759-9954

摘要：Porous polybenzimidazole networks PBI-1 and PBI-2 were synthesized through a one-step polycondensation of 3,3'-diaminobenzidine with tris(4-carboxyphenyl) amine and tetrakis(4-carboxyphenyl)silane, respectively. The polymerizations proceeded smoothly under mild conditions and were completed within a short reaction time. Using CO2 as a probe molecule, the analyses of CO2 adsorption isotherms reveal that the resultant polybenzimidazole networks belong to ultramicroporous polymers with pore sizes centered at around 5 angstrom. Compared to PBI-2, PBI-1 composed of triphenylamine units shows a larger Henry's constant, first virial coefficient and heat of adsorption, indicating a stronger affinity for CO2. As a result, it displays a significantly higher CO2 uptake of up to 13.2 wt% at 273 K and 1 bar. In addition, for PBI-1, the uptake capacities of benzene and water vapors are as high as 54.4 wt% and 32.9 wt%, respectively, whereas that of hexane vapor is only 1.0 wt%, exhibiting the potential applications in benzene recovery and selective removal of water from alkane solvents.