Influence of Cutting Heat on Quality of Drilling of Carbon/Epoxy Composites

Hits:

Indexed by:期刊论文

Date of Publication:2012-09-01

Journal:MATERIALS AND MANUFACTURING PROCESSES

Included Journals:SCIE、EI、Scopus

Volume:27

Issue:9

Page Number:968-972

ISSN No.:1042-6914

Key Words:Carbon; Composites; Damage; Drilling; Epoxy; Heat; Modulus; Temperature

Abstract:Cutting heat generated during drilling of carbon/epoxy composites has been recognized as a factor to influence the machine quality. This research aims to study the damage induced by cutting heat during drilling. A temperature-dependent experiment was carried out. The temperature of specimen was changed, and the machine parameter was constant in the experiment. The material temperature near exit was measured. Besides, the machine quality was detected, and the failure mode of the machined surface was observed. The results show that the decrease of material stiffness with increasing temperature induces the decrease of machine quality. Furthermore, delamination, transverse crack, high porosity, and fuzzing are mainly caused by low material stiffness. The transverse cracks which join together under cutting force lead to the generation of spalling on exit surface. As temperature increases, the failure modes of the machined surface changes from matrix dominant failure to interface dominant failure. It is predicted that the critical material temperature of damage-free is 186 degrees C.

Pre One:大型复合材料构件数字化加工工装与装置的开发与应用

Next One:C/E复合材料螺旋铣削制孔方法抑制缺陷产生的机理