Microwave Absorption of gamma '-Fe-2.6 Ni1.4N Nanoparticles Derived from Nitriding Counterpart Precursor
点击次数：
论文类型：期刊论文
发表时间：2012-04-01
发表刊物：JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY
收录刊物：SCIE、EI、PubMed、Scopus
卷号：12
期号：4
页面范围：3040-3047
ISSN号：1533-4880
关键字：Nitride Nanoparticles; Arc Discharge; Permittivity; Permeability; Microwave Absorption
摘要：gamma-Fe2.6Ni1.4 nanoparticles were prepared by the arc-discharge method as the precursor and its nitride counterpart of gamma'-Fe2.6Ni1.4N nanoparticles was synthesized directly through a thermal ammonolysis reaction at the temperature of 673 K for two hours. The resultant product was identified as a homogeneous ternary nitride with nearly spherical shape and average size of about 60.0 nm. The electromagnetic characteristics of gamma'-Fe2.6Ni1.4N derivant and gamma-Fe2.6Ni1.4 precursor have been studied in the frequency range of 2-18 GHz. Compared with the precursor, gamma'-Fe2.6Ni1.4N nanoparticles exhibits an enhanced electromagnetic absorption property resulted from the increased dielectric loss by nitriding process. The optimal reflection loss (RL) of gamma'-Fe2.6Ni1.4N nanoparticles/paraffin composite can reach -39.9 dB at 5.2 GHz in a thickness of 2.29 mm, and the frequency band corresponding RL < -10 dB is over 2.6-18 GHz in the thickness range of 0.78-4.20 mm.
发表时间：2012-04-01