论文名称：MECHANICAL PROPERTIES OF HOT-PRESSED B(4)C-SiC COMPOSITES
论文类型：会议论文
收录刊物：EI、CPCI-S
卷号：220
页面范围：189-196
关键字：boron carbide; composites; mechanical properties
摘要：Monolithic B(4)C and B(4)C-SiC ceramic composites were prepared by hot-pressing technology. The microstructure and mechanical properties of sintered samples were studied. The results showed that the samples reached full density under the sintering condition of 2000 degrees C and 30MPa. For monolithic B(4)C, the highest hardness of 36.7Gpa, and fracture toughness of 7.11MPa m(1/2) were obtained. In B(4)C -10%SiC composite, the highest flexural strength of nearly 700MPa was measured. The influence mechanism of SiC addition on the mechanical properties of composites was discussed.
发表时间：2010-01-01