论文名称:多晶硅太阳能电池片的回收再利用研究 论文类型:期刊论文 发表刊物:无机材料学报 所属单位:材料科学与工程学院 卷号:33 期号:09 页面范围:987-992 ISSN号:1000-324X 摘要:Recovering Si material from the degraded solar cells is significant for environmental protection and material recycling. In this study, the optimal conditions for recycling degraded solar cells by chemical etching and ultrasonic cleaning were investigated. The samples were tested by EDS, SEM and XPS, The results showed that Al electrodes were completely removed from cells by reaction with 10wt% NaOH solution for 18 min, with less silicon corrosion lost. After that, Ag electrodes were completely exfoliated from the cells by ultrasonic cleaning (40 kHz) for 20 min. Si3N4 film was thoroughly eliminated after the cells were etched with 40wt% HF solution for 10 min, which was proved to be the optimal reaction time. A quantitative experiment was performed in this study with 8. 9068 g cells. The results show that the recycling mass of Al electrodes, Ag electrodes and Si wafers are 1.1102 g, 0.0766 g and 7.7169 g, respectively. 备注:新增回溯数据 发表时间:2022-06-29