论文名称：Effect of Zn addition on primary silicon morphology and B distribution in Si-Al alloy
论文类型：期刊论文
发表刊物：JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
收录刊物：SCIE、EI
卷号：25
期号：4
页面范围：1751-1756
ISSN号：0957-4522
摘要：Si-Al-Zn alloy melts were used for silicon purification by the solvent refining process. The effect of metal Zn addition on alloy macrostructure, primary Si morphology, as well as B distribution in Si-Al alloy during solvent refining process was studied in this work. The three main results were as follows. First, with the increasing of Zn content in Si-Al alloy, the primary silicon changed from slender plate-like to irregular and short, meanwhile the distribution of primary silicon changed from bottom to central and top. Second, the more Zn content in Si-Al alloy, the more inclusions of eutectic melts will be in primary silicon, which results in diffusion difficulty of impurity B in inclusions. Third and last, with increasing Zn content, the refining ratio of B increased gradually and removal fraction of B decreased accordingly.
发表时间：2014-04-01