论文名称：Preparation and properties of nano-SiC strengthening Al2O3 composite ceramics
论文类型：期刊论文
发表刊物：MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
收录刊物：SCIE、EI
卷号：528
期号：6
页面范围：2246-2249
ISSN号：0921-5093
关键字：Al2O3-SiC; Polycarbosilane; Flexural strength; Fracture toughness
摘要：The processing and mechanical behaviors of Al2O3-xwt.%SiC(x = 1,2,5, ASx) nano-composites prepared by the in situ synthesis of SiC from polycarbosilane (PCS) were investigated. The composites were densified by hot pressing. The microstructure and mechanical properties of the sintered composites were analyzed. The results showed that a fully dense structure was obtained when a few nano-SiC were doped and that the fracture toughness and strength were highly improved compared with those of monolithic Al2O3. The fracture toughness reached 5.1 MPa m(1/2) in AS2 composite. The maximum flexural strength was 516 MPa obtained in AS1 composite. (C) 2010 Elsevier B.V. All rights reserved.
发表时间：2011-03-15