论文名称：Mechanical properties of hot-pressed Al2O3/SiC composites
论文类型：期刊论文
发表刊物：MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
收录刊物：SCIE、EI
卷号：527
期号：18-19
页面范围：4646-4649
ISSN号：0921-5093
关键字：Al2O3/SiC composites; Flexural strength; Fracture toughness
摘要：Al2O3/SiC composites were prepared by hot pressing with micrometer Al2O3 powders and SiC powders as raw materials. The mechanical properties, including flexural strength, hardness, and fracture toughness were studied. The experimental results showed that flexural strength was enhanced with the density increasing and grain refining. 615 MPa, the highest flexural strength was obtained in 20 wt.%SiC composite sintered at 1735 degrees C. The fracture toughness increased at first then decreased with SiC content variation. 7.6 MPa m(1/2) of the highest fracture toughness was obtained in the composite containing 5 wt.%SiC sintered at 1635 degrees C. (C) 2010 Elsevier B.V. All rights reserved.
发表时间：2010-07-15