点击次数：

发布时间：2019-03-11

论文类型：期刊论文

发表时间：2016-06-12

发表刊物：14th China International Nanoscience and Technology Symposium / Nano-products Exposition

收录刊物：Scopus、CPCI-S、EI、SCIE

卷号：172

期号：1,SI

页面范围：59-65

ISSN号：1058-4587

关键字：Cu-containing Fe-Ni; corrosion-resistant alloy; new phase and double-cluster structure model

摘要：In order to recognize the mechanisms of corrosion resistance in Cu-containing Fe-Ni alloys, two experimental composition 39.0Ni-57.1Fe-3.9Cu and 39.4Ni-57.7Fe-2.9Cu (at.-%) were designed according to the double-cluster model. The corrosion resistance measurements indicated that the alloy 39.0Ni-57.1Fe-3.9Cu possessed equal corrosion resistance to conventional steels 304 while the corrosion resistance of 39.4Ni-57.7Fe-2.9Cu was deteriorated by a new secondary precipitate phase. Observation by transmission electron microscopy and energy dispersive X-ray spectrometer showed evidence of the new phase in alloy 39.4Ni-57.7Fe-2.9Cu which having a crystal structure in a face-centered-cubic (FCC) symmetry and owning parameter a = 8.2 angstrom. A possible atomic composition was confirmed to be 16.8Ni-74.9Fe-8.3Cu.