发表刊物：JOURNAL OF ENERGY CHEMISTRY

收录刊物：SCIE、ISTIC、CSCD

卷号：25

期号：3

页面范围：539-544

ISSN号：2095-4956

关键字：ZSM-48; Alkali treatment; Hydroisomerization; Mesopore; Hexadecane

摘要：ZSM-48 zeolites with various Si/Al ratios were hydrothermally synthesized in the H2N(CH2)(6)NH2 (HDA)-containing media. The obtained samples were highly crystallized with minor mixed phases as evidenced by X-ray powder diffraction (XRD). The alkaline treated ZSM-48 zeolites maintained its structure under different concentrations of NaOH aqueous solution. Micropores remained unchanged while mesopores with wide pore size distribution formed after the alkaline treatment. The surface area increased from 228 to 288 m(2)/g. The Bronsted acid sites had little alteration while an obvious increase of Lewis acid sites was observed. The hydroisomerization of hexadecane was performed as the model reaction to test the effects of the alkali treatment. The conversion of hexadecane had almost no change, which was attributed to the preservation of the Bronsted acid sites. While high selectivity to iso-hexadecane with an improved iso to normal ratio of alkanes was due to the mesopore formation and improved diffusivity. (C) 2016 Science Press and Dalian Institute of Chemical Physics. All rights reserved.