Indexed by:期刊论文
Date of Publication:2021-01-10
Journal:FERROELECTRICS
Volume:565
Issue:1,SI
Page Number:26-34
ISSN No.:0015-0193
Key Words:Environmental catalysis; activity; metal-organic framework; Cu plus; Ni-MOF; selective catalytic reduction
Abstract:A series of Cu+/Ni-MOF materials with different Cu loading were prepared by a hydrothermal method and were applied on selective catalytic reduction with NH3-SCR. From characterization results of XRD, XPS and TPR, it could be inferred that Cu(+)species have been successfully introduced into the Ni-MOF framework. Compared with monometallic Ni-MOF catalyst, all bimetallic Cu+/Ni-MOF sample showed much better NH3-SCR activity at low temperature and achieved about 30% increase in the maximum catalytic efficiency at 320 degrees C, which indicating a good synergistic effect between copper and nickel ions.
Pre One:Synthesis and characterization of bimetallic Cu-Al-BTC MOFs as an efficient catalyst for selective catalysis reduction of NO with CO
Next One:Acetate production from inorganic carbon (HCO3-) in photo-assisted biocathode microbial electrosynthesis systems using WO3 /MoO3/g-C3N4 heterojunctions and Serratia marcescens species