高强钢低功率脉冲激光诱导熔化极活性气体保护电弧仰焊成形
点击次数:
发表时间:2020-01-01
发表刊物:Zhongguo Jixie Gongcheng/China Mechanical Engineering
卷号:31
期号:17
页面范围:2137-2141
ISSN号:1004-132X
摘要:A low-power pulsed laser induced metal active gas(MAG) arc hybrid welding tests in overhead positions were carried out for 5mm thick E36 high strength steel plates. The results show that heat input of laser induced MAG arc hybrid welding is 29% lower than that of single arc welding. By reducing weld pool sizes, hybrid welding may effectively inhibit the formation of concave defects, and then increase the processsing parameter ranges. Tensile tests and bending tests show that the welding joints without internal concave defects have good static tensile strength and bending load. Static tensile strength of the welding joints with internal concave is equivalent to the base metal, but the maximum bending load is significantly reduced. © 2020, China Mechanical Engineering Magazine Office. All right reserved.
备注:新增回溯数据