Pulsed MIG welding of AZ31B magnesium alloy

点击次数:

论文类型:期刊论文

发表时间:2011-02-01

发表刊物:MATERIALS SCIENCE AND TECHNOLOGY

收录刊物:Scopus、SCIE、EI

卷号:27

期号:2

页面范围:518-524

ISSN号:0267-0836

关键字:Magnesium alloy; Pulsed MIG welding; Microstructure; Mechanical property

摘要:Pulsed metal inert gas welding of AZ31B magnesium alloy is carried out, and continuous butt joints of high quality are obtained at optimised parameters. The effects of parameters on weld formation and welding stability are studied. The microstructure, mechanical properties and fracture of weld beads with different filler wires are investigated. The results show that it is a stable drop transition process with optimised parameters, which belongs to globular transfer. The precipitates in fusion zone and heat affected zone (HAZ) are uniform, dispersive and almost granular. The grain size in fusion zone is fine, and the grain size does not grow too large in HAZ compared with the base metal. The ultimate tensile strength of weld beads can be 94% of base metal, and the average elongation is 11%. Dimples and coarse tearing ridges can be observed on the fracture of the weld bead.