A comparative study of ZnO film and nanorods for ZnO/polyfluorene inorganic/organic hybrid junction
点击次数：
论文类型：期刊论文
发表时间：2012-09-05
发表刊物：JOURNAL OF ALLOYS AND COMPOUNDS
收录刊物：SCIE、EI、Scopus
卷号：534
页面范围：1-5
ISSN号：0925-8388
关键字：ZnO; Composite materials; Optical properties
摘要：Both ZnO nanorods (NRs) and film were combined with spin-coated polyfluorene (PF) organic films to form ZnO/PF hybrid junctions on ITO glass substrates. A comparative study was performed through quantitative analysis of the as-grown hybrid junctions with ZnO film and NRs structure, respectively. In general, both devices exhibited a rectifying diode-like behavior as expected from the n-ZnO/p-PF nature. Nevertheless, the ZnO NRs based hybrid device has a great advantage over the film based device in view of interface quality and rectifying behavior. These results indicate that the ZnO NRs based inorganic/organic hybrid junctions is more suitable and preferred for the potential application in optoelectronic devices. (C) 2012 Elsevier B. V. All rights reserved.
上一条：Liquid Crystalline Perylene Diimide Outperforming Non liquid Crystalline Counterpart: Higher Power Conversion Efficiencies (PCEs) in Bulk Heterojunction (BHJ) Cells and Higher Electron Mobility in Space Charge Limited Current (SCLC) Devices
下一条：High optical quality ZnO films grown on graphite substrate for transferable optoelectronics devices by ultrasonic spray pyrolysis