点击次数：

论文类型：期刊论文

发表时间：2009-04-01

发表刊物：OPTICAL MATERIALS

收录刊物：SCIE、EI

卷号：31

期号：6

页面范围：889-894

ISSN号：0925-3467

关键字：Near-infrared; Organic light-emitting diodes; Electroluminescence

摘要：Red and near-infrared (NIR) organic light-emitting devices (OLEDs) were fabricated based on Tetra (2-Isopropyl-5-methylphenoxyl) substituted metal-free phthalocyanine (Tetra-H(2)Pc). The devices were fabricated by vacuum deposition and spin coating methods. The electroluminescence (EL) intensity at about 910 nm in the devices based on Tetra-H(2)Pc was increased by about 14 times compared with the intensity at about 930 nm in the devices based on unsubstituted metal-free phthalocyanine (H(2)Pc) in the same device structures. The improvement in the EL intensity was attributed to the large steric hindrance of non-peripheral phenoxyl substituent of Tetra-H2Pc. It was found that the NIR EL spectra of the doped devices exhibited a strong dependence on the concentration of Tetra-H2Pc. The emission at 740 nm was from Tetra-H(2)Pc monomer, while the emissions around 910 nm and 870 nm were from excimer or higher aggregated species. (C) 2008 Elsevier B.V. All rights reserved.