点击次数：

论文类型：会议论文

发表时间：2010-11-06

收录刊物：EI、CPCI-S、SCIE、Scopus

卷号：150-151

页面范围：229-+

关键字：fiber reinforced cementitious composite; tensile strain hardening; ductility index; longitudinal reinforcement ratio; energy

摘要：Ultra-high toughness cementitious composite (UHTCC) is a PVA fiber reinforced cementitious composite. Tensile strain hardening behavior with ultimate tensile strain of more 3% under direct tensile loading is one of its important characteristics. In the current article, nine simply-supported reinforced UHTCC beams were subjected to four-point bending loading to experimentally investigate the influence of ductile deformation behavior of UHTCC on ductility capacity of reinforced structural members. Ductility index is determined by adopting three different parameters, i.e., deformation capacity, energy dissipation capacity as well as curvature capacity. The effect of longitudinal tensile reinforcement ratios on the variation of ductility in UHTCC reinforced beams was examined. It was found from the experimental results that the combination of ductile matrix (UHTCC) and steel bar prevents from occurrence of localized cracks in pure bending zone, snowing high damage tolerance and ductile failure behavior. The results also show that: as longitudinal tensile reinforcement ratio increases, deformation ductility and curvature ductility both exponentially decrease while a small reduction is demonstrated for energy ductility at ultimate failure.