点击次数：

论文类型：期刊论文

发表时间：2016-09-12

发表刊物：SCIENTIFIC REPORTS

收录刊物：SCIE、PubMed、Scopus

卷号：6

页面范围：33241

ISSN号：2045-2322

摘要：Multishelled NiO hollow microspheres for high-performance supercapacitors have been prepared and the formation mechanism has been investigated. By using resin microspheres to absorb Ni2+ and subsequent proper calcinations, the shell numbers, shell spacing and exterior shell structure were facilely controlled via varying synthetic parameters. Particularly, the exterior shell structure that accurately associated with the ion transfer is finely controlled by forming a single shell or closed exterior double-shells. Among multishelled NiO hollow microspheres, the triple-shelled NiO with an outer single-shelled microspheres show a remarkable capacity of 1280 F g(-1) at 1 A g(-1), and still keep a high value of 704 F g(-1) even at 20 A g(-1). The outstanding performances are attributed to its fast ion/electron transfer, high specific surface area and large shell space. The specific capacitance gradually increases to 108% of its initial value after 2500 cycles, demonstrating its high stability. Importantly, the 3S-NiO-HMS//RGO@Fe3O4 asymmetric supercapacitor shows an ultrahigh energy density of 51.0 Wh kg(-1) at a power density of 800 W kg(-1), and 78.8% capacitance retention after 10,000 cycles. Furthermore, multishelled NiO can be transferred into multishelled Ni microspheres with high-efficient H-2 generation rate of 598.5 mL H-2 min(-1) g(-1) Ni for catalytic hydrolysis of NH3BH3 (AB).