The Precipitation Behavior and Hot Deformation Characteristics of Electron Beam Smelted Inconel 740 Superalloy

Hits:

Indexed by:期刊论文

Date of Publication:2018-04-01

Journal:JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE

Included Journals:SCIE、EI

Volume:27

Issue:4

Page Number:1580-1591

ISSN No.:1059-9495

Key Words:740 superalloy; electron beam smelting; hot deformation; precipitation

Abstract:The Inconel 740 superalloy was prepared by the electron beam smelting (EBS) technology, the precipitation behavior and strengthening mechanism were studied, and the hot deformation characteristics of EBS 740 superalloy were investigated. The results indicate that the EBS 740 superalloy is mainly strengthened by the mechanism of weakly coupled dislocation shearing, and the resulting critical shear stress is calculated to be 234.6 MPa. The deformation parameters show a great influence on the flow behavior of EBS 740 superalloy. The strain rate sensitivity exponent increases with the increasing of deformation temperature, and the strain hardening exponent shows a decreasing trend with the increasing of strain. The activation energy of EBS 740 above 800 A degrees C is measured to be 408.43 kJ/mol, which is higher than the 740H superalloy. A hyperbolic-sine-type relationship can be observed between the peak stress and Zener-Hollomon parameter. Nevertheless, the influence of deformation parameters is found to be considerably different at temperatures below and above 800 A degrees C. The size of dynamic recrystallization (DRX) grains decreases with the increasing of strain rate when the strain rate is lower than 1/s, and reverse law can be found at higher strain rate. As a result, a piecewise function is established between the DRX grain size and hot working parameters.

Pre One:Effect of solution heat treatment on microstructure and electrochemical behavior of electron beam smelted Inconel 718 superalloy

Next One:材料科学基础MOOC平台课程建设及学习效果探讨