发表刊物：Chemical communications (Cambridge, England)

收录刊物：SCIE

卷号：54

期号：39

页面范围：4979-4982

ISSN号：1364-548X

摘要：Many nonprecious metal-selenide-based materials have been reported as electrocatalysts with high activity for the oxygen evolution reaction (OER). Herein, a hybrid catalyst film composed of Cu2Se and Cu2O nanoparticles directly grown on Ti foil (Cu2Se-Cu2O/TF) was prepared through a simple and fast cathodic electrodeposition method. Surprisingly, this electrode required a relatively low overpotential of 465 mV to achieve a catalytic current density of 10 mA cm-2 for the OER in 0.2 M carbonate buffer (pH = 11.0). Furthermore, a long-term constant current electrolysis test confirmed the high durability of the Cu2Se-Cu2O/TF anode at a current density of 10 mA cm-2 over 20 h. The XRD, TEM and XPS analysis of the sample after the OER indicated that a CuO protective layer formed on the surface of the Cu2Se-Cu2O catalyst, which effectively suppressed further oxidation of the Cu2Se-Cu2O catalyst during the OER and resulted in sustained catalytic oxidation of water.