High temperature corrosion and microstructure deterioration of KHR35H radiant tubes in continuous annealing furnace

Hits:

Indexed by:期刊论文

Date of Publication:2012-04-01

Journal:ENGINEERING FAILURE ANALYSIS

Included Journals:SCIE、EI

Volume:21

Page Number:59-66

ISSN No.:1350-6307

Key Words:Heat resistant steel; Oxidation; Creep; Microstructure deterioration

Abstract:High temperature corrosion and microstructure deterioration phenomenon of KHR35H radiant tubes had been investigated after a service life of approximately 2 years in annealing process. Analyses revealed that deterioration in mechanical properties of the radiant tube was caused primarily by significant growth of precipitates during high temperature service. Internal oxidation and simultaneously in situ carbides dissolution were responsible for the formation of large number of voids and microcracks at the inner wall of the tubes, which brought the reduction of effective thickness of the tube wall and may act as crack sources under either thermal shock or creep deformation. (C) 2011 Elsevier Ltd. All rights reserved.

Pre One:SnAgCu焊料中Sn元素在模拟土壤溶液中的浸出行为

Next One:Sn-0.75Cu钎料接头在NaCl溶液中的电化学腐蚀行为