Three-Layer Al/Al-B4C Composite Material Prepared by Casting and Hot Rolling

点击次数:

论文类型:期刊论文

发表时间:2015-11-01

发表刊物:POWDER METALLURGY AND METAL CERAMICS

收录刊物:SCIE、EI、Scopus

卷号:54

期号:7-8

页面范围:390-396

ISSN号:1068-1302

关键字:three-layer composite; Al; B4C; hot rolling; clad ratio

摘要:Casting and hot rolling are proposed to verify a semi-continuous casting and hot rolling process to produce a three-layer Al/Al-B (4) C metal-cermet composite. The outer layer is pure Al, the inner layer is Al matrix composite reinforced with B (4) C particles (the mass fraction of Al and B (4) C are 62.36 and 37.64%, respectively). The results show that the reinforced particles are distributed in the inner layer homogeneously, and both layers are sintered together with no pores or flaws. The clad ratios of the composites of 26, 5, 3, and 1 mm are 50.28, 54.67, 61.23, and 57.46%, respectively. The Vickers hardness varies from 46 HV for the outer pure aluminum layer to 158 HV for the inner composite layer in 3 mm specimen, indicating totally different properties in different layers.