Microstructure and mechanical properties of Al-1Mn and Al-10Si alloy circular clad ingot prepared by direct chill casting
- 点击次数：
- 论文类型：期刊论文
- 发表时间：2013-01-20
- 发表刊物：MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES
MICROSTRUCTURE AND PROCESSING
- 收录刊物：SCIE、EI
- 文献类型：J
- 卷号：561
- 页面范围：239-244
- ISSN号：0921-5093
- 关键字：Direct chill casting; Aluminum alloys; Clad ingot; Microstructure;
Mechanical properties; Interface
- 摘要：An innovative direct chill casting process to prepare Al-10 wt%Si and Al-1 wt%Mn alloy circular clad ingots has been developed in the present study. The experimental casting parameters were determined by theoretical analysis, numerical simulation and experimental processes. The interface of clad ingots was investigated by methods of metallographic examination, electron probe microanalysis (EPMA) and transmission electron microscopy (TEM). The results showed that excellent metallurgical bonding of two different aluminum alloys could be achieved by direct chill casting. The Al-1Mn alloy which was poured into the mold earlier served as the substrate for heterogeneous nucleation of Al-10Si alloy. Because of diffusion of Si and Mn elements, a diffusion lager with a thickness of about 40 mu m on average between the Al-10Si and Al-1Mn alloys could be obtained. The tensile strength of the clad ingot was 106.8 MPa and the fractured position was located in the Al-1 Mn alloy side, indicating the strength of the interfacial region is higher than that of Al-1Mn alloy. Crown Copyright (C) 2012 Published by Elsevier B.V. All rights reserved.