Trivalent cobalt complex mediated formation of stereoregular CO2 copolymers from phenyl glycidyl ether

点击次数:

论文类型:期刊论文

发表时间:2013-08-21

发表刊物:POLYMER CHEMISTRY

收录刊物:SCIE、EI、Scopus

卷号:4

期号:16

页面范围:4425-4433

ISSN号:1759-9954

摘要:Trivalent cobalt-based catalyst systems have proven to be efficient for the coupling of CO2 with epoxides to afford the corresponding polycarbonates with perfectly alternating nature. Particularly, the single-component Co(III)-Salen complexes with an intramolecular cocatalyst exhibit excellent activity and selectivity for the formation of polycarbonates from various epoxides even at very low catalyst loading. Herein, we report the synthesis of CO2 copolymers from phenyl glycidyl ether using the Co(III)-Salen complex with an appended 1,5,7-triazabicyclo[4.4.0] dec-5-ene (designated as TBD) as a catalyst. The resulting polymers have more than 99% carbonate linkage and possess unprecedented head-to-tail content. Comparative kinetic studies were performed via in situ infrared spectroscopy as a function of temperature to evaluate the activation barriers for the production of polycarbonate versus cyclic carbonate involving two Co(III)-based catalyst systems. The energies of activation determined for cyclic carbonate and copolymer formation in the coupling reaction of CO2 and phenyl glycidyl ether catalyzed by the binary 1/PPNDNP system are 72.8 and 39.2 kJ mol(-1), respectively, compared to the corresponding values of 104.6 and 30.2 kJ mol(-1) with the single-component catalyst 3. The big difference in the energies of activation for cyclic carbonate versus copolymer formation accounts for the excellent selectivity for copolymer formation in the single-component catalyst systems even at elevated temperatures. Furthermore, with the use of enantiopure phenyl glycidyl ether, highly stereoregular polycarbonate with >99% isotacticity and >99% head-to-tail content could be obtained. Importantly, the completely isotactic copolymer is a typical semicrystalline thermoplastic, which possesses a melting point of 75 degrees C.