点击次数：

论文类型：期刊论文

发表时间：2017-03-01

发表刊物：SCRIPTA MATERIALIA

收录刊物：SCIE、EI

卷号：129

页面范围：20-24

ISSN号：1359-6462

关键字：Eutectic ceramic; Al2O3/ZrO2(Y2O3); Crystal growth; Constitutional supercooling

摘要：The addition of more components are an interesting way of the microstructural controls. Herein, adding Y2O3 to Al2O3-ZrO2 bulk eutectic at the low G/v ratio (thermal gradient G divided by growth rate v) was adopted to tailor the morphology. As the Y2O3 content increases, the solidification structure changes obviously from cellular into the, dendritic shape. Especially, a typical irregular Al2O3/ZrO2/Y3Al5O12 (YAG) ternary eutectic appeared in the inter -colony region for the higher Y2O3 content. This microstructure transition is consistent with the classical constitutional supercooling criterion. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.