A series of sulfonic acid functionalized mixed-linker DUT-4 analogues: synthesis, gas sorption properties and catalytic performance

论文类型:期刊论文

发表时间:2017-11-07

发表刊物:DALTON TRANSACTIONS

收录刊物:SCIE、EI

卷号:46

期号:41

页面范围:14356-14364

ISSN号:1477-9226

摘要:In this work, we present the successful synthesis of a series of sulfonic acid functionalized mixed-linker metal-organic frameworks (MOFs) having the DUT-4 topology by using different ratios of 2,6-naphthalene-dicarboxylic acid (H-2-NDC) and 4,8-disulfonaphthalene-2,6-dicarboxylic acid (H-2-NDC-2SO(3)H) in one-pot reactions. The obtained materials were fully characterized and their CO2 adsorption properties at low and high pressures were studied and compared with those of the pristine DUT-4 material. Generally, the CO2 adsorption capacities range from 3.28 and 1.36 mmol g(-1) for DUT-4 to 1.54 and 0.78 mmol g(-1) for DUT-4-SO3H (50) up to 1 bar at 273 K and 303 K, respectively. Computational calculations corroborated the structural changes of the material in function of the loading of sulfonic acid groups. Furthermore, due to the strong Bronsted acid character, the resulting sulfonic acid based MOF material was evaluated as a catalyst for the ring opening of styrene oxide with methanol as a nucleophile under mild conditions, showing almost full conversion (99%) after 5 hours of reaction. A hot filtration experiment demonstrated that the catalysis occurred heterogeneously and the catalyst could be recovered and reused for multiple runs without significant loss in activity and crystallinity.

上一条: A fluorine-containing hydrophobic covalent triazine framework with excellent selective CO2 capture performance

下一条: Grafting of a Eu3+-tfac complex on to a Tb3+-metal organic framework for use as a ratiometric thermometer