点击次数：

论文类型：期刊论文

发表时间：2017-03-21

发表刊物：CATALYSIS SCIENCE & TECHNOLOGY

收录刊物：SCIE、EI

卷号：7

期号：6

页面范围：1333-1341

ISSN号：2044-4753

摘要：Transition metal carbides have been of great interest because of their noble-metal-like properties. Because of the complexity of their structures, it is crucial to design an experiment that can eliminate the influence of supports, surface carbon contamination and particle sizes when finding the exact catalytic active sites. In this work, phase-pure W2C nanorods (lengths of 2-4 mu m and diameters of 100-600 nm) with different amounts of crystal defects were prepared by the pyrolysis of metatungstate and melamine hybrid nanorods with nanoscale periodic structure synthesized in the aqueous phase. The nanoscale alternating structure between tungsten oxide and melamine effectively promotes the reduction of tungsten oxide and the formation of tungsten carbide, avoiding the deposition of carbon on the surface. At the same time, vacancy defects are generated due to the deficiency of carbon. High pyrolysis temperature (900 degrees C), prolonged pyrolysis time (4 h), introduction of hydrogen and the proper increase of the temperature ramping rate (5 degrees C min-1) are favorable to the formation of vacancy defects. The activities of different catalysts were evaluated by the hydrodeoxygenation of benzofuran at 320 to 350 degrees C. The results show that the vacancy defect sites in W2C are the key to the high reactivity of W2C. The vacancy defect sites have favorable properties for the cleavage of carbon-oxygen bonds. The Caromatic-O bond is cleaved in the case of unsaturated aromatic rings, thereby reducing the consumption of hydrogen. In addition, it is found that the apparent activation energy of each chemical bond is linear-like and positively related to its bond dissociation energy.