Grain nucleation and growth behavior of a Sn-Pb alloy affected by direct current: An in situ investigation

发表时间:2019-03-11 点击次数:

论文名称:Grain nucleation and growth behavior of a Sn-Pb alloy affected by direct current: An in situ investigation
论文类型:期刊论文
发表刊物:JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
收录刊物:Scopus、SCIE、EI
卷号:33
期号:10
页面范围:1134-1140
ISSN号:1005-0302
关键字:Sn-Pb alloy; Synchrotron X-ray radiography; Solidification; Microstructure; Electric current
摘要:In situ synchrotron X-ray radiography was used to study the effect of direct current ( DC) on the grain nucleation and growth of Sn-50 wt.% Pb alloy. The results showed that applying DC adequately during solidification could effectively enhance the grain nucleation and inhibit its growth. Imaging of comparative experiments with varying DC intensity indicated that the final grain size, determined by the competition between grain nucleation and growth, was sensitively dependent on the DC intensity. It was found that the average grain size was decreased from 1632 to 567 mu m with DC density of 1.5 A/mm(2) compared to the case without DC. Beyond this value, raising the current density may cause a significant decrease in the nucleation rate, and thus lead to a coarsening of the grain structure. (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.