Characteristics of copper-clad aluminum rods prepared by horizontal continuous casting
- 点击次数：
- 论文类型：期刊论文
- 发表时间：2017-11-01
- 发表刊物：METALS AND MATERIALS INTERNATIONAL
- 收录刊物：SCIE
- 卷号：23
- 期号：6
- 页面范围：1197-1203
- ISSN号：1598-9623
- 关键字：composites; casting; interfaces; mechanical properties; computer
simulation
- 摘要：An innovative horizontal continuous casting method was developed and successfully used to prepare copper-clad aluminum (CCA) rods with a diameter of 85 mm and a sheath thickness of 16 mm. The solidification structure and element distribution near the interface of the CCA ingots were investigated by means of a scanning electron microscope, an energy dispersive spectrometer, and an electron probe X-ray microanalyzer. The results showed that the proposed process can lead to a good metallurgical bond between Cu and Al. The interface between Cu and Al was a multilayered structure with a thickness of 200 mu m, consisting of Cu9Al4, CuAl2, alpha-Al/CuAl2 eutectic, and alpha-Al + alpha-Al/CuAl2 eutectic layers from the Cu side to the Al side. The mean tensile-shear strength of the CCA sample was 45 MPa, which fulfills the requirements for the further extrusion process. The bonding and diffusion mechanisms are also discussed in this paper.
- 发表时间：2017-11-01