Semisolid-rolling and annealing process of woven carbon fibers reinforced Al-matrix composites
- 点击次数：
- 论文类型：期刊论文
- 发表时间：2017-07-01
- 发表刊物：JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
- 收录刊物：EI、SCIE、Scopus
- 卷号：33
- 期号：7
- 页面范围：623-629
- ISSN号：1005-0302
- 关键字：Metal-matrix composites; Woven carbon fiber; Semisolid-rolling process;
Annealing; Mechanical property
- 摘要：Semisolid-rolling method was successfully developed to prepare the Ni-coated woven carbon fibers reinforced Al-matrix composite. Due to the appropriate matrix flowability and rolling pressure, the Al-matrix could infiltrate into the woven fibers sufficiently and attach to the reinforcements closely forming a smooth interface. The rolling speed of 4 rad/min offered a subtle equilibrium between the heat transfer and the material deformation. The covering matrix should be controlled at semisolid state to provide a better infiltration behavior and a protective effect on the carbon fibers. With the addition of fibers, an improvement for more than 25% was obtained in the bending strength of the materials. Furthermore, the woven carbon fibers could strengthen the composite in multiple directions, rather than only along the fiber longitudinal directions. The annealing process promoted the Ni coating to react with and to diffuse into the matrix, resulted in an obvious increase of the bending strength. (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
- 发表时间：2017-07-01