y Effect of green preform composition, temperature and duration conditions on microstructure and performance of Al-5Ti-0.2C master alloy
- 点击次数：
- 论文类型：期刊论文
- 发表时间：2016-02-01
- 发表刊物：INTERNATIONAL JOURNAL OF MATERIALS RESEARCH
- 收录刊物：SCIE、EI、Scopus
- 卷号：107
- 期号：2
- 页面范围：168-176
- ISSN号：1862-5282
- 关键字：Al-Ti-C master alloy; Grain refinement; Self-propagating
high-temperature synthesis; Macrostructure; EDS linear scanning
- 摘要：Al-5Ti-0.2C master alloy was prepared via a simple combustion synthesis approach. By means of different smelting parameters, changes in its microstructure and refining performance were studied. Under short holding conditions (5 - 10 min) increase of Al content in the preform from 10 % to 40 % results in more numerous carbon-rich particles in the master alloy and better refinement performance. Nevertheless, preparation of refiner with satisfactory refining ability requires longer holding conditions (30 min). With prolonged holding time after the combustion, alloys possess similar microstructure and refining efficacy regardless of the chemical composition of the preform. Decrease of smelting temperature from 1 250 degrees C to 950 degrees C results in noticeable deterioration of the master alloy refining performance. The reasons, which impede successful utilization of primary benefits provided by combustion reaction, are discussed.
- 发表时间：2016-02-01