点击次数：

论文类型：期刊论文

发表时间：2018-01-01

发表刊物：JOURNAL OF CATALYSIS

收录刊物：SCIE、EI

卷号：357

页面范围：118-126

ISSN号：0021-9517

关键字：Hydrogen peroxide; Electrocatalysis; Oxygen reduction reaction; Fluorine species; Hierarchically porous carbon

摘要：Electrochemical synthesis of hydrogen peroxide (H2O2) via two-electron pathway of oxygen reduction reaction is a promising alternative to the current anthraquinone process. The H2O2 production from O-2 is a competing reaction with four-electron O-2 reduction to H2O, and the selectivity is related to the adsorption energy of the OOH intermediate on electrocatalysts surface. Generally, the properties for binding of OOH intermediate on catalysts can be controlled by changing its electronic structure. Herein, the electronic structure of porous carbon materials was tuned by doping different types and contents of fluorine species. The yield of H2O2 generation depended on the F content and the best catalytic activity toward H2O2 electrosynthesis was obtained with F content of 3.41 at.%. The resultant F-doped porous carbon (FPC) catalysts exhibited good H2O2 selectivity of 97.5-83.0% and the H2O2 production rate could reach 112.6-792.6 mmol h(-1) g(-1) over the potential range of 0.2 V to -0.3 vs. RHE (pH 1). The density functional theory (DFT) calculations and experiments revealed that the incorporation of CF2,3 into carbon plane promotes the activation of O-2 molecule and facilitates desorption of OOH intermediate, which was crucial to H2O2 synthesis. (C) 2017 Elsevier Inc. All rights reserved.