论文类型：会议论文

发表时间：2016-10-02

收录刊物：EI、Scopus

卷号：874

页面范围：323-327

摘要：A nanotwinned surface is formed on a titanium alloy under nanoindentations. Prior to nanoindentation, blocks of a ternary titanium alloy are machined by chemical mechanical polishing. The surface roughness Ra and peak-to-valley values are 1.135 nm and 8.82 nm, respectively. The hardness in the indented surface is greatly increased, indicated from the load-displacement curves compared to the polished surfaces. Nanotwins are confirmed using transmission electron microscopy. The nanotwinned surface is uniformly generated by nanoindentations at room temperature, which is different from previous findings, in which high temperature, high pressure, or chemical reagents are usually used. The nanotwinned surface is produced by pure mechanical stress, neither material removal nor addition. ? 2016 Trans Tech Publications, Switzerland.