A comparative study of ZnO film and nanorods for ZnO/polyfluorene inorganic/organic hybrid junction
点击次数：
论文类型：期刊论文
发表时间：2012-09-05
发表刊物：JOURNAL OF ALLOYS AND COMPOUNDS
收录刊物：SCIE、EI、Scopus
卷号：534
页面范围：1-5
ISSN号：0925-8388
关键字：ZnO; Composite materials; Optical properties
摘要：Both ZnO nanorods (NRs) and film were combined with spin-coated polyfluorene (PF) organic films to form ZnO/PF hybrid junctions on ITO glass substrates. A comparative study was performed through quantitative analysis of the as-grown hybrid junctions with ZnO film and NRs structure, respectively. In general, both devices exhibited a rectifying diode-like behavior as expected from the n-ZnO/p-PF nature. Nevertheless, the ZnO NRs based hybrid device has a great advantage over the film based device in view of interface quality and rectifying behavior. These results indicate that the ZnO NRs based inorganic/organic hybrid junctions is more suitable and preferred for the potential application in optoelectronic devices. (C) 2012 Elsevier B. V. All rights reserved.