Environment-friendly, flame retardant thermoplastic elastomer-magnesium hydroxide composites
发布时间：2019-03-12
点击次数：
- 论文类型：
- 期刊论文
- 发表时间：
- 2017-08-01
- 发表刊物：
- FUNCTIONAL MATERIALS LETTERS
- 收录刊物：
- Scopus、EI、SCIE
- 文献类型：
- J
- 卷号：
- 10
- 期号：
- 4
- ISSN号：
- 1793-6047
- 关键字：
- Thermoplastic elastomer; magnesium hydroxide; magnesium oxide; flame retardant performance
- 摘要：
- Halogen-free and environment-friendly magnesium hydroxide (Mg(OH)(2)) was synthesized to enhance the flame retardant properties of thermoplastic elastomer (TPE). When the Mg(OH)(2) content was optimized to 35 wt.%, the TPE-Mg(OH)(2) composites exhibited the best flame retardant properties. The results showed that there was a delay of ignition time of the samples containing Mg(OH)(2); compared with the samples without Mg(OH)(2), the heat release rate and total heat release decrease by 31.4% and 35.6%, while total smoke production and mass loss rate reduce by 56% and 34.2%, respectively. This work opens a door to manufacture fire-resistant polymer-based composites with environmental-friendly flame retardant additives by controllable crystallization and chemical strategies.
- 第一作者
- Tang, Hao
- 合写作者
- Guo, Xinwen,Xue, Dongfeng,Li, Xiaonan,Ao, Man,Chen, Kunfeng
- 通讯作者
- Xue, DF (reprint author), Dalian Univ Technol, Sch Chem Engn, Dalian 116024, Peoples R China.; Xue, DF (reprint author), Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Rare Earth Resource Utilizat, Changchun 130022, Jilin, Peoples R China.