Facile Synthesis of Mesoporous Reduced Graphene Oxide Microspheres with Well-Distributed Fe2O3 Nanoparticles for Photochemical Catalysis
发表时间：2019-03-12
点击次数：
- 论文类型：
- 期刊论文
- 第一作者：
- Xu, Zehai
- 通讯作者：
- Zhang, GL (reprint author), Zhejiang Univ Technol, Inst Ocean & Environm Chem Engn, State Key Lab Breeding Base Green Chem Synth Tech, Hangzhou 310014, Zhejiang, Peoples R China.
- 合写作者：
- Li, Wanbin,Zhang, Yufan,Xue, Zhen,Guo, Xinwen,Zhang, Guoliang
- 发表时间：
- 2016-10-12
- 发表刊物：
- INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH
- 收录刊物：
- SCIE、EI、Scopus
- 文献类型：
- J
- 卷号：
- 55
- 期号：
- 40
- 页面范围：
- 10591-10599
- ISSN号：
- 0888-5885
- 摘要：
- In this study, we report the fabrication of hollow reduced graphene oxide microspheres with well-distributed Fe2O3 nanoparticles (Fe-rGOS) via a spray-drying methodology. L-Ascorbic acid was-employed to reduce graphite oxide (GO) and improve velocity of electrons transfer. Because of L-ascorbic acid and the spray-drying procedure, the in situ Fe2O3 nanoparticles with a mean size of 5-10 nm were uniformly deposited on rGO support and the rGO migrated to the surface of the drop to form microspheres. The well dispersed nanoparticles not only generated more active sites-and interface contact which was beneficial to enhance the stability of catalysts but also acted as pillars between the rGO layers to achieve mesoporous structure. The formed mesoporous frameworks enhanced mass transfer to a large extent and led to the much better catalytic efficiency. Therefore, the prepared Fe-rGOS exhibited a remarkable photocatalytic activity in a wide pH range and superior recyclability with low leaching of iron ions.