高硅ZSM-5原粉的外表面改性及其在甲醇制丙烯反应中的应用（英文）
发表时间：2025-06-03
点击次数：
- 第一作者：
- 赵学斌
- 通讯作者：
- 洪杨,王林英,樊栋,闫娜娜,刘晓娜,田鹏,郭新闻,刘中民
- 发表时间：
- 2022-10-09
- 发表刊物：
- 催化学报
- 文献类型：
- J
- 卷号：
- 39
- 期号：
- 08
- 页面范围：
- 1418-1426
- ISSN号：
- 0253-9837
- 摘要：
- Post-synthetic treatment of high-silica as-made ZSM-5 with organic template in the micropores was explored to reduce/remove the external surface acid density of ZSM-5. It is found that Na(2)H(2)EDTA treatment can selectively remove the surface Al atoms, but generates new acid sites (likely silanol nests) on the external surface. H3PO4 treatment is unable to remove surface Al atoms, while small amount of P is left on the external surface, which effectively decreases the acid density. The catalytic performance of the resultant materials is evaluated in the methanol conversion reaction. H3PO4 treatment can effectively improve both the catalytic lifetime and the stability of propene selectivity. This occurs due to a combination of the increased tolerance to the external coke deposition and the depressed coking rate (reduced side reactions). Na(2)H(2)EDTA treatment only prolongs the catalytic lifetime, resulting from the improved tolerance to the external coke deposition. Under the optimized H3PO4 treatment condition, the resultant ZSM-5 gives a catalytic lifetime of about 1.5 times longer than the precursor. Moreover, the propene selectivity is improved, showing a slight increasing trend until the deactivation. (C) 2018, Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. All rights reserved.
- 备注：
- 新增回溯数据
- 是否译文：
- 否