Role of Hydrothermal parameters on phase purity of orthorhombic LiMnO2 for use as cathode in Li ion battery
发布时间：2019-03-09
点击次数：
- 论文类型：
- 期刊论文
- 发表时间：
- 2015-06-01
- 发表刊物：
- CERAMICS INTERNATIONAL
- 收录刊物：
- EI、SCIE
- 文献类型：
- J
- 卷号：
- 41
- 期号：
- 5
- 页面范围：
- 6729-6733
- ISSN号：
- 0272-8842
- 关键字：
- Li-ion battery; Cathode materials; Hydrothermal synthesis; Charge-discharge test; LiMnO2
- 摘要：
- Orthorhombic LiMnO2 (o-LiMnO2) was prepared under hydrothermal conditions using sol gel derived Mn2O3 and LiOH as precursors and the effects of hydrothermal reaction parameters such as reaction temperature and LiOH and Mn2O3 concentrations on the phase purity of o-LiMnO2 were studied. The as-prepared samples were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and galvanostatic charge discharge tests. Phase purity of o-LiMnO2 was affected by hydrothermal temperature and LiOH and Mn2O3 concentrations. High LiOH concentration facilitated the synthesis of pure phase o-LiMnO2. Low reaction temperature, lower than 140 degrees C, did not lead to the formation of pure phase of o-LiMnO2. Galvanostatic charge discharge test results showed that pure o-LiMnO2 had larger discharge capacity than the mixed phases of o-LiMnO2 and Li2MnO3. However, the cycling performance of the mixed phases of o-LiMnO2 with Li2MnO3 was found to be better than that of pure o-LiMnO2. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
- 第一作者
- Li, Keyan
- 合写作者
- Xue, Dongfeng,Guo, Xinwen,Komarneni, Sridhar,Shua, Fenfen,Zhang, Jiawei,Chen, Kunfeng
- 通讯作者
- Xue, DF (reprint author), Dalian Univ Technol, Sch Chem Engn, Dalian 116024, Peoples R China.