点击次数：

论文类型：期刊论文

发表时间：2016-03-10

发表刊物：SCIENTIFIC REPORTS

收录刊物：SCIE、PubMed

卷号：6

页面范围：22893

ISSN号：2045-2322

摘要：Metals with nanoscale twins have shown ultrahigh strength and excellent ductility, attributed to the role of twin boundaries (TBs) as strong barriers for the motion of lattice dislocations. Though observed in both experiments and simulations, the barrier effect of TBs is rarely studied quantitatively. Here, with atomistic simulations and continuum based anisotropic bicrystal models, we find that the long-range interaction force between coherent TBs and screw dislocations is negligible. Further simulations of the pileup behavior of screw dislocations in front of TBs suggest that screw dislocations can be blocked kinematically by TBs due to the change of slip plane, leading to the pileup of subsequent dislocations with the elastic repulsion actually from the pinned dislocation in front of the TB. Our results well explain the experimental observations that the variation of yield strength with twin thickness for ultrafine-grained copper follows the Hall-Petch relationship.