论文类型: 期刊论文
发表时间: 2019-12-01
发表刊物: CERAMICS INTERNATIONAL
收录刊物: EI、SCIE
卷号: 45
期号: 17
页面范围: 22759-22764
ISSN号: 0272-8842
关键字: TiO2; Milling; Functional applications; Impedance
摘要: The multi-walled carbon nanotubes (MWCNTs)-anatase composites were prepared by ball-milling method. The influence of milling conditions (dry-milling or wet-milling) on the phases, morphology, dispersion, and electromagnetic wave absorption properties of the samples was studied. After characterization, the results indicated that ball-milling process had little effect on the phase and the grain size of anatase. The dispersion of MWCNTs in MWCNTs-anatase composites for wet-milling was preferable to that for dry-milling. The composites prepared by dry-milling method had an excellent electromagnetic wave absorbing property. The minimum value of RL was -37.3 dB at 6.1 GHz with the thickness of 3 mm, and the effective bandwidth was 6.1 GHz for the thickness in the range of 2-5 mm. Debye relaxation process, eddy current loss, and impedance matching were the main reasons for the electromagnetic wave absorption of the composites. The MWCNTs-anatase composites could be an easy obtained wave absorption materials.