Fine powder grown from liquid-phase nitrates explosive

点击次数:

论文类型: 会议论文

发表时间: 2021-07-22

页面范围: 425-+

摘要: Nanostructured spinel lithium manganese oxide (LiMnO) with about 20 nm in diameter was synthesized for the first time by explosive method. The detonation products were characterized by scanning electron microscopy. Powder X-ray diffraction and transmission electron microscopy were used to characterize the products. Lithium manganate with spherical morphology and more uniform secondary particles, with smaller primary particles of diameters from 10 to 20 nm and a variety of morphologies were found. Lithium manganate with a fine spherical morphology different from that of the normal spinel is formed after detonation wave treatment due to the very high quenching rate. It might also provide a cheap large-scale synthesis method. Explosive detonation is strongly nonequilibrium processes, generating a short duration of high pressure and high temperature. Free metal atoms are first released with the decomposition of explosives, and then theses metal and oxygen atoms are rearranged, coagulated and finally crystallized into lithium manganate during the expansion of detonation process. For detonation of the water-solubility explosive, the detonation pressure, the detonation temperature and the adiabatic gamma were 2-5 GPa, 2000-3000 K and close to 3.

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学