点击次数：

发布时间：2019-03-09

论文类型：期刊论文

发表时间：2010-08-20

发表刊物：MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

收录刊物：Scopus、EI、SCIE

卷号：527

期号：21-22

页面范围：6098-6101

ISSN号：0921-5093

关键字：W-Cu; Nanocomposites; Dynamic consolidation; Ball-milling; Density

摘要：It would be possible to produce nanostructured systems via dynamic consolidation due to the short duration. In the study, the bulk W-25%Cu nanocomposites were fabricated by the technique of dynamic consolidation. The nanostructured W-Cu powder was prepared by hydrogen-reduction of ball-milled W and CuO. The results indicated that the consolidated composites had a final density of 97.6% T.D. and the W crystalline sizes were measured as 27 nm. The W-Cu composites showed the homogeneous microstructure and were composed entirely of W and Cu. The fracture surface was analyzed by SEM and showed intergranular fracture. The hardness was measured. It is proved that it is feasible to fabricate nanostructured W-Cu composites by dynamic consolidation. (C) 2010 Elsevier B.V. All rights reserved.