论文类型: 期刊论文
发表时间: 2008-07-01
发表刊物: COMBUSTION EXPLOSION AND SHOCK WAVES
收录刊物: SCIE、EI
卷号: 44
期号: 4
页面范围: 491-496
ISSN号: 0010-5082
关键字: amorphous alloys; explosive welding; temperature field; collision point velocity
摘要: The feasibility of bonding amorphous ribbons via explosive welding (EW) is demonstrated. With 20-120 layers of Fe78B13Si9 and Fe(40)Ni(40)P14B(6) amorphous ribbons 25 mu m thick and 10 cm wide, the plate samples are bonded by using two settups with a collision point velocity of 3900-4800 m/sec and a flyer plate velocity of 570900 m/sec. The largest area of the bonded sample is 30 cm(2). The microstructures of the samples are observed by optical microscopy and X-ray diffractometry. Based oil the formation characteristics of amorphous alloys and heat-exchange characteristics during the EW process, a square-wave model for the temperature distribution across the interface is proposed. It can be used to explain the reasons for the samples keeping the amorphous state across the interface after explosive welding. The calculated results are in good agreement with the experiments.