论文类型：期刊论文
发表时间：2021-02-25
发表刊物：MATERIALS & DESIGN
卷号：195
ISSN号：0264-1275
关键字：Mode-I fracture toughness; Double cantilever beam test; Trilinear traction-separation law; Automated fiber placement
摘要：Interlaminar fracture toughness is an important parameter to characterize the delamination performance of car bon fiber-reinforced epoxy laminates. In this study, the mode-I fracture toughness of interlaminar interfaces with different local ply angles were studied by experiments and numerical simulations. A set of double cantilever beam specimens of T800 carbon fiber/EH104 epoxy were prepared according to the ASTM-D5528-01 standard, where four specimens had straight ply interfaces (0 degrees//0 degrees, 15 degrees//-15 degrees, 30 degrees//-30 degrees, and 45 degrees//-45 degrees) and two specimens had curved ply interfaces (curvature radius: 300 and 500 mm). The mode-I fracture toughness was characterized using a data reduction scheme based on the modified beam theory. The results revealed that the mode-I fracture toughness values for the specimens with a curved ply interface were significantly higher than those for specimens with a straight ply interface. (c) 2020 The Author(s). Published by Elsevier Ltd. This is an open access article under the CC BY license (http:// creativecommons.org/licenses/by/4.0/).