- Quantitative inspection of iron contamination on 304 Austenitic stainless steel
- 点击次数：
- 论文类型： 会议论文
- 发表时间： 2011-01-01
- 收录刊物： CPCI-S
- 页面范围： 175-179
- 关键字： Stainless steel; Iron contamination; Quantitative inspection; Electrochemical corrosion
- 摘要： The iron contaminated sample of 304 Austenitic stainless steel and a clean sample after chemical passivation was chosen to introduce a new method for quantitative inspection on iron contamination, and the relationship between evaluation results and the character parameter of electrochemical corrosion was analyzed. The result showed that the measured a* value from the inspection increased with increasing iron contaminant, while the a* is close to zero for the chemical passived sample. Although the measured a* was decreased after the contaminated samples was exposed in air and 3.5 wt.% NaCl solution, the inspection method can still quatitatively evaluate on the iron contaminant. The a* value has a linear relationship with the corrosion potential and breakdown potential from electrochemical polarization test. It was conformed that the chromogenic quantitative inspection method could adequately evaluate on the iron contamination.