Effect of Surface Fe-Sn Intermetallics on Oxide Films Formation of Stainless Steel in High Temperature Water
点击次数:
论文类型: 期刊论文
发表时间: 2018-04-01
发表刊物: HIGH TEMPERATURE MATERIALS AND PROCESSES
收录刊物: SCIE、EI
卷号: 37
期号: 4
ISSN号: 0334-6455
关键字: stainless steel; low melting point metal Sn; oxidation; SR-GIXRD; electrochemical impedance spectra
摘要: The oxidation of stainless steel with Fe-Sn intermetallics adhesion in 300 degrees C water was studied by analyzing the morphologies and phase structures of surface oxide films. The oxidation behavior of stainless steel was discussed in order to illustrate the effect of Fe-Sn intermetallics on the oxidation characteristic. Larger size of faceted spinel and small size of SnO2 particles are observed on the samples with Fe-Sn intermetallics adhesion, whereas smaller faceted hematite and spinel grow on the samples without Fe-Sn intermetallics adherence. The surface intermetallics aggravates the spalling of oxide particles and decreases the corrosion resistance of stainless steel. Such deterioration is attributed to the loose microstructure characteristic and the poor corrosion resistance of SnO2 particles formed in high temperature water.

程从前

副教授   博士生导师   硕士生导师

任职 : 院长助理,中国腐蚀与防护学会高温专业委员会委员,中国机械工程学会理化检验分委员会委员,辽宁省化工学会腐蚀与防护专业委员会委员

性别: 男

毕业院校:大连理工大学

学位: 博士

所在单位:材料科学与工程学院

学科:材料学

电子邮箱:cqcheng@dlut.edu.cn

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学
访问量: 手机版 English 大连理工大学 登录

开通时间:..

最后更新时间:..