The effect of thickness on the creep properties of a single-crystal nickel-based superalloy
点击次数:
论文类型: 期刊论文
发表时间: 2018-06-13
发表刊物: MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
收录刊物: SCIE
卷号: 728
页面范围: 124-132
ISSN号: 0921-5093
关键字: Creep; Single crystal; Oxidation; Internal nitrides; Voids; Crack
摘要: Creep rupture tests were conducted at 980 degrees C/250 MPa on specimens with different wall thickness values obtained from a single-crystal nickel-based superalloy. Experimental results showed that the thin specimens had an inferior creep life compared with the thick ones. All specimens were oxidised during the creep tests. Electron probe microanalysis and scanning electron microscopy combined with energy-dispersive X-ray spectroscopy revealed that internal nitrides developed in the y'-free zone and even in the matrix. The presence of internal nitrides induced the nucleation of creep voids and initiation of cracks during creep rupture, thereby increasing the growth rate of cracks and facilitating the failure of the creep specimens. The morphology of the fracture sections indicated that the interaction of cracks and creep damage also contributed to this phenomenon. Cracks played an important role in the creep behaviour of the thin specimens, and creep damage effectively influenced that of the thick specimens.

程从前

副教授   博士生导师   硕士生导师

任职 : 院长助理,中国腐蚀与防护学会高温专业委员会委员,中国机械工程学会理化检验分委员会委员,辽宁省化工学会腐蚀与防护专业委员会委员

性别: 男

毕业院校:大连理工大学

学位: 博士

所在单位:材料科学与工程学院

学科:材料学

电子邮箱:cqcheng@dlut.edu.cn

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学
访问量: 手机版 English 大连理工大学 登录

开通时间:..

最后更新时间:..