Interaction Mechanism between Zn and Passivated Stainless Steel
点击次数：
发布时间： 2019-03-13
发布时间：2019-03-13
论文类型：期刊论文
发表时间：2019-01-01
发表刊物：INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
收录刊物：Scopus、SCIE
卷号：14
期号：1
页面范围：301-314
ISSN号：1452-3981
关键字：Solid Zn; Stainless steel; Passivation; XPS; Mott-Schottky
摘要：This study investigated the interaction between solid Zn and passivated stainless steel. The effect of passivation film on the interaction mechanism of Zn and stainless steel surface was determined. The cross section morphology and the chemical compositions of the intermetallics (IMC) were detected by scanning electron microscopy (SEM) and energy dispersive X-ray spectrometer (EDX). The composition and integrity of the passivation films were identified by X-ray photoelectron spectroscopy (XPS) and Mott-Schottky electrochemical analysis. Results showed that solid Zn reacted with stainless steel by forming interfacial columnar delta phase (Fe, Cr, Ni)Zn-10 with tiny granule zeta phase (Fe, Cr, Ni)Zn-13 IMCs. The reaction was hindered by the chemical passivation film and the native oxide film grown in air; the influence of the former is significantly higher than that of the latter. The passivation films were composed of Fe-rich and Cr-rich oxides and hydroxides. The chemical passivation film was richer in Cr oxides and hydroxides and had higher integrity than the native oxide film. The IMCs formed between the low-melting-point-metal and stainless steel can be attributed to the incomplete passivation films, which impeded the compound layer growth to some extent. The passivation film served as a physical barrier between solid Zn and stainless steel.

程从前

同专业博导 同专业硕导 个人学术主页

副教授   博士生导师   硕士生导师

任职 : 院长助理，中国腐蚀与防护学会高温专业委员会委员，中国机械工程学会理化检验分委员会委员，辽宁省化工学会腐蚀与防护专业委员会委员

性别： 男

毕业院校：大连理工大学

学位： 博士

所在单位：材料科学与工程学院

学科：材料学

电子邮箱：

辽ICP备05001357号 地址：中国·辽宁省大连市甘井子区凌工路2号 邮编：116024
版权所有：大连理工大学
访问量： 手机版 English 大连理工大学 登录

开通时间：..

最后更新时间：..