- Microstructure Evolution and Nitridation in an As-Cast 25Cr-35Ni-1Mo Radiant Tube After Long-Term Service
- 点击次数：
- 论文类型： 期刊论文
- 发表时间： 2012-12-01
- 发表刊物： METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- 收录刊物： Scopus、SCIE、EI
- 卷号： 43A
- 期号： 12
- 页面范围： 4525-4531
- ISSN号： 1073-5623
- 摘要： The microstructure evolution of 25Cr-35Ni-1Mo radiant tubes was investigated after approximately two years of service in a continuous annealing furnace. The inner and outer tube walls were exposed to N-2-containing combustion environment and protective atmosphere, respectively. The decarburization feature analysis indicated that carbon content decreased toward the tube surface. However, precipitates at the inner and outer walls were coarser, their content increased and the microhardness value also increased compared to that in the central area. X-ray diffraction illustrated that M-2(C,N) and M-6(C,N) were the dominant carbide at the inner and outer walls, and precipitates in the central area were mainly M23C6 and M-6(C,N) phases. The results were assumed to be associated with the nitridation phenomenon that occurred in the N-2-containing environment at elevated temperatures.