发表刊物：FRONTIERS OF ENVIRONMENTAL SCIENCE & ENGINEERING

收录刊物：Scopus、SCIE

卷号：8

期号：2

页面范围：180-187

ISSN号：2095-2201

关键字：graphene; palladium; debromination; BDE-47

摘要：Graphene electrodes (Ti/Gr) were prepared by depositing Gr sheets on Ti substrate, followed by an annealing process for enhancing the adhesion strength. Electrochemical impedance spectroscopies and X-ray diffraction patterns displayed that the electrochemical behavior of Ti/Gr electrodes can be improved due to the generation of TiO2 layer at Ti-Gr interface during the annealing process. The palladized Gr electrodes (Ti/Gr/Pd) were prepared by electrochemical depositing Pd nanoparticles on Gr sheets. The debromination ability of Ti/Gr/Pd electrodes was investigated using BDE-47 as a target pollutant with various bias potentials. The results indicated that the BDE-47 degradation rates on Ti/Gr/Pd electrodes increased with the negative bias potentials from 0 V to -0.5 V (vs. SCE). Almost all of the BDE-47 was removed in the debromination reaction on the Ti/Gr/Pd electrode at -0.5 V for 3 h, and the main product was diphenyl ethers, meaning it is promising to debrominate completely using the Ti/Gr/Pd electrode. Although the debromination rate was slightly slower at -0.3 V than that under -0.5 V, the current efficiency at -0.3 V was higher, because the electrical current acted mostly on BDE-47 rather than on water.